Solvalitt Midtherm Alu Silicone Heat-Resistant Aluminium Paint is a high-temperature coating, in the silicone coating system. Recommended as a topcoat with a suitable primer system for use under insulation. Suitable for suitably prepared carbon steel, galvanised steel, stainless steel and aluminium. Parameters on this page: volume solids 34 ± 2%, dry film thickness 20-40 µm, theoretical spreading rate 17-8.5 m²/L. Comparable models from the same brand: Solvalitt 300 Alu silicone heat-resistant aluminium paint, Solvalitt 300 silicone heat-resistant paint, Solvalitt 600 Alu silicone high-temperature aluminium paint.
Parameter source: JOTUN original technical data sheet (TDS) for Solvalitt Midtherm Alu Silicone Heat-Resistant Aluminium Paint; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 34 ± 2% |
|---|---|
| Dry Film Thickness | 20–40 µm |
| Theoretical Spreading Rate | 17-8.5 m²/L |
| VOC | 567 g/L (China) |
| Density / Specific Gravity | 1 kg/L |
| Number of Components | One-component |
| Flash Point | 27 °C |
| Thinner | JOTUN Thinner No. 7 / JOTUN Thinner No. 10 |
| Gloss | Matt (0–35) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Silicone heat-resistant aluminium coating
It is a one-component physically drying silicone acrylic coating. The product contains aluminium flake pigment. Resistant to high temperatures up to 260 °C. In atmospheric environments it can be used as a primer, intermediate coat or topcoat. Suitable for suitably prepared carbon steel, galvanised steel, stainless steel and aluminium.
Industrial protective coatings:
Specifically a heat-resistant coating. Suitable for insulated and uninsulated surfaces. Recommended as a topcoat over a suitable primer system for use under insulation.
Others
Silicone Heat-Resistant Coating
For the different products in this series, refer to the respective technical data sheets
Aluminium
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 34± 2 % |
| Gloss (GU 60°) | ISO 2813 | Matt (0–35) |
| Flash Point | ISO 3679 Method 1 | 27 °C |
| Density | Theoretical Value | 1 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | Calculation | 576 g/L |
| Hong Kong | Air Pollution Control (VOC) Regulation | Calculation | 576 g/L |
| EU | European Paint Directive 2004/42/CE | Calculation | 576 g/L |
| China | Mandatory national standard of China | GB 30981.2-2025 | 567 g/L |
| Coating hazards GB | 30981.2-S-Pb≤1000-NC |
The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 20–40 µm |
| Wet Film Thickness | 60–120 µm |
| Theoretical Spreading Rate | 17-8.5 m²/L |
Surface Preparation
| Substrate | Minimum | Recommended |
| Carbon Steel | Sa 2½ (ISO 8501-1) | |
| Stainless steel | With the nozzle pressure reduced, hold the nozzle at 45–60° to the vertical and sweep blast the surface with an approved non-metallic abrasive to produce a sharp angular surface profile. | |
| Aluminium | The surface should be abraded by hand or machine using a non-metallic abrasive, fibre discs or abrasive paper to produce scratch marks. | Dry abrasive blast clean to SSPC-SP 13 / NACE No. 6. |
| Galvanised steel | The surface should be clean, dry and have a suitable profile | Sweep blast with a non-metallic abrasive to produce a clean, |
| ° | a rough and uniform surface. | |
| Coated surface | A clean, dry and sound compatible primer. | |
This product may be applied by the following methods
| Spray: | Apply by air spray or airless spray. |
| Brush: | Recommended for touch-up and small-area application. Take care to achieve the specified dry film thickness. |
One-component
| Thinner | JOTUN Thinner No. 7 / JOTUN Thinner No. 10 |
|---|
| Nozzle tip size (inch/1000): | 15-17 |
| Nozzle pressure (minimum): | 100 bar/1450 psi |
| Substrate Temperature | 5 °C | 10 °C | 23 °C | 40 °C |
| Touch Dry | 45 min | 30 min | 15 min | 10 min |
| Walk-on Dry | 4 h | 3 h | 2 h | 1 h |
| Minimum recoat interval | 6 h | 3 h | 2 h | 1 h |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
The mechanical properties of a freshly applied Solvalitt film are slightly reduced. This can be improved by heating the paint system to 200 °C for about 1 hour.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Temperature
| Continuous | Peak | |
| Drying, atmospheric | 260°C | - |
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Epoxy, zinc silicate, silicone acrylic |
| Subsequent coat: | Silicone acrylic |
| Volume | Container Size | |
| (L) | ||
| Silicone heat-resistant aluminium coating | 5 | |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
Silicone Heat-Resistant Aluminium Paint 24 months
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.