SeaQuantum XT FW Methacrylic Silane Low-Friction Self-Polishing Antifouling Coating belongs to Antifouling, Acrylic system. As an ultra-high-end solution, SeaQuantum XT FW is designed for vessels focused on protection performance in high-fouling environments, carbon emission reduction, biodiversity protection and fuel savings. SeaQuantum XT FW is derived from the proven silane and methacrylic silane resin antifouling technology of the SeaQuantum series, which has completed more than 20,000 application projects worldwide. Parameters on this page: Volume Solids 59 ± 2%, Dry Film Thickness (DFT) 75–175 µm, Theoretical Spreading Rate 7.9–3.4 m²/L.
Parameter source: JOTUN original Technical Data Sheet (TDS) “SeaQuantum XT FW Methacrylic Silane Low-Friction Self-Polishing Antifouling Coating”; values such as spreading rate are converted according to TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 59 ± 2% |
|---|---|
| Dry Film Thickness | 75–175 µm |
| Theoretical Spreading Rate | 7.9–3.4 m²/L |
| VOC | 371 g/L (EU) |
| Density / Specific Gravity | 1.7 kg/L |
| Number of Components | One-component |
| Flash Point | 25 °C |
| Thinner | JOTUN Thinner No. 7 / Jotun Thinner No. 10 |
| Wet Film Thickness | 130–300 µm |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
SeaQuantum XT FW
SeaQuantum XT FW is a single-component chemically hydrolysing methacrylic silane antifouling coating employing advanced technology, providing protection performance for vessels in high-fouling environments.
SeaQuantum XT FW is derived from the proven silane and methacrylic silane resin antifouling technology of the SeaQuantum series, which has completed more than 20,000 application projects worldwide.
SeaQuantum XT FW incorporates ActiCore™ core technology — a unique patented resin technology combined with an optimised biocide combination, providing sustained and stable algae and slime protection. The coating forms an ultra-smooth initial surface and provides performance over the complete cycle. With highly predictable and stable self-polishing performance, it provides in-service performance.
Application of SeaQuantum XT FW shall follow the instructions in the JOTUN HPS (Hull Performance Solutions) workflow.
For details, consult your local JOTUN office.
| Marine coatings | Suitable for newbuilding underwater hulls (outfitting conditions suitable for fresh water). |
|---|
SeaQuantum XT FW can be applied at zero degrees.
As an ultra-high-end solution, SeaQuantum XT FW is designed for vessels focused on protection performance in high-fouling environments, carbon emission reduction, biodiversity protection and fuel savings.
This antifouling coating is designed for long service life; as part of a complete coating system, its service life can reach up to 90 months. Suitable for dry-docking maintenance and newbuilding underwater hulls (meeting seawater or fresh water outfitting conditions).
Designed for service in high-fouling environments.
Antifouling.
Complies with the IMO Antifouling Systems Convention AFS/CONF/26 and IMO MEPC.331(76)
Other certificates and approvals are available on request.
Deep red, light red
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 59± 2 % |
| Flash Point | ISO 3679 Method 1 | 25 °C |
| Density | Theoretical Value | 1.7 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| EU | European Paint Directive 2004/42/CE | Calculation | 371 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
Typical recommended specification range
| Dry Film Thickness | 75–175 µm |
| Wet Film Thickness | 130–300 µm |
| Theoretical Spreading Rate | 7.9–3.4 m²/L |
| Maximum total dry film thickness of a multi-coat antifouling system | 600 µm |
|---|
Surface Preparation
| Substrate | Minimum | Recommended |
| Coated surface | New tie coat or antifouling: remove any contamination affecting adhesion of the intermediate coat. | |
| Exceeding the maximum recoat interval may require cleaning, abrading or the use of another coating, as appropriate. | ||
| Aged antifouling coatings with a leached layer: | ||
| Rinse thoroughly with fresh water at a minimum nozzle pressure of 200 bar | Rinse thoroughly with fresh water at a minimum nozzle pressure of 340 bar | |
| remove. | ||
This product may be applied by the following methods
| Spray: | Apply by airless spray. |
| Brush: | usable. Take care to achieve the specified dry film thickness. |
| Roller: |
One-component
| Thinner | JOTUN Thinner No. 7 / Jotun Thinner No. 10 |
|---|
| Nozzle tip size (inch/1000): | 21-31 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
| Substrate Temperature | -10 °C | 0 °C | 10 °C | 23 °C | 40 °C |
| Touch Dry | 8 h | 2 h | 45 min | 30 min | |
| Minimum recoat interval | 27 h | 16 h | 9 h | 7 h | 6 h |
| Dry/cured to immersion | 39 h | 24 h | 10 h | 9 h | 8 h |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
The dry/cure-to-immersion data in the table above are the times required before the product can enter service. For baffles and similar equipment, longer drying times are required. Refer to the application procedure for further advice.
At higher film thicknesses, the antifouling film stays soft longer. To ensure hull roughness readings, doubling the minimum immersion time is recommended when two or more coats of antifouling are applied in rapid succession.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to immersion: the minimum time before the coating can be permanently immersed in sea water.
Suitable anti-corrosive primer system. The recommended tie coat for the subsequent antifouling is:
Safeguard Universal ES Vinyl Epoxy (0QZ)
or
Safeguard Plus Vinyl Epoxy (5BP)
| Volume | Container Size | |
| (L) | ||
| SeaQuantum XT FW Methacrylic Silyl Low-friction Self-smoothing Antifouling | 20 | |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
The storage temperature shall not exceed 35 °C.
SeaQuantum XT FW 9 months Methacrylic Silane Low-Friction Self-Smoothing Antifouling Paint
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.