Penguard Pro GF Universal Abrasion-resistant Epoxy Glass Flake Paint is a glass flake coating in the epoxy system. Recommended for offshore environments, including splash zones, refineries, power stations, bridges, buildings and mining equipment. Suitable for suitably prepared carbon steel, stainless steel, aluminium, galvanized steel, concrete and thermally sprayed zinc substrates. Parameters on this page: volume solids 75 ± 2%; dry film thickness 150–600 µm; theoretical spreading rate 5–1.3 m²/L. Comparable products from the same brand: Jotacote Xtend GF Ultra-high-solids Abrasion-resistant Epoxy Glass Flake Paint, Jotamastic 87 GF Low-surface-preparation Epoxy Abrasion-resistant Glass Flake Paint, Jotamastic 90 GF Low-surface-preparation Epoxy Abrasion-resistant Glass Flake Paint 90.
Source: JOTUN original technical data sheet (TDS) 'Penguard Pro GF Universal Abrasion-resistant Epoxy Glass Flake Paint'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 75 ± 2% |
|---|---|
| Dry Film Thickness | 150–600 µm |
| Theoretical Spreading Rate | 5–1.3 m²/L |
| VOC | 180 g/L (China) |
| Density / Specific Gravity | 1.4 kg/L |
| Number of Components | Two-component |
| Flash Point | 32 °C |
| Thinner | Jotun Thinner No. 17 |
| Mixing Ratio | 3 parts : 1 part (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Penguard Pro GF
A two-component amine-cured abrasion-resistant epoxy glass flake coating. A high-build product featuring low surface preparation requirement and high solids. Dedicated to all-area general-purpose use on new construction. Can be used as a primer, intermediate coat, topcoat or single-coat system in atmospheric and immersed environments. Suitable for suitably prepared carbon steel, stainless steel, aluminium, galvanized steel, concrete and thermally sprayed zinc substrates.
Suitable for steel structures and pipes in highly corrosive and immersed environments. Recommended for offshore environments, including splash zones, refineries, power stations, bridges, buildings and mining equipment.
Designed as a general-purpose product in coating systems, with better durability. Within a certain dry film range and application area, this product has high flexibility. Dedicated to areas requiring abrasion and impact resistance, such as decks, walkways and helidecks.
Others
Pre-qualified in the selected coating system in accordance with NORSOK M-501. Other certificates and approvals are available on request.
Penguard Pro — General-Purpose Abrasion-Resistant High-Build Epoxy (0B4)
Penguard Pro Alu — General-Purpose Abrasion-Resistant Epoxy Aluminium High-Build (0G6)
For the different products in this series, refer to the respective technical data sheets
Many other colours are available
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 75± 2 % |
| Gloss (GU 60°) | ISO 2813 | Semi-gloss (35–70) |
| Flash Point | ISO 3679 Method 1 | 32 °C |
| Density | Theoretical Value | 1.4 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | Calculation | 226 g/L |
| Hong Kong | Air Pollution Control (VOC) Regulation | Calculation | 227 g/L |
| EU | European Paint Directive 2004/42/CE | Calculation | 227 g/L |
| China | Mandatory national standard of China | GB 30981.2-2025 | 180 g/L |
Coating hazards GB 30981.2-S-Pb≤1000-NC. Contains reactive thinner. The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 150–600 µm |
| Wet Film Thickness | 200–800 µm |
| Theoretical Spreading Rate | 5–1.3 m²/L |
Surface Preparation
| Substrate | Minimum | Recommended |
| Carbon Steel | St 2 (ISO 8501-1) | Sa 2½ (ISO 8501-1) |
| Stainless steel | The surface should be blasted with a non-metallic abrasive, | “Blast clean using an approved non-metallic abrasive |
| hand- or machine-sanded using abrasive paper or fibre discs, | to produce a sharp angular surface profile.” |
to produce scratch marks on the surface.
| Aluminium | The surface should be abraded by hand or machine using a non-metallic abrasive, fibre discs or abrasive paper to produce scratch marks. | |
| Galvanised steel | The surface should be clean, dry and have a suitable profile | Sweep blast with a non-metallic abrasive to produce a clean, |
| ° | a rough and uniform surface. | |
| Shop-primed Steel | Dry, clean, intact shop primer | Sweep blast or abrasive blast clean at least 70% of the area to Sa 2 (ISO 8501-1) |
| Concrete | Curing time of at least 4 weeks. Maximum moisture 5%. For existing | Curing time of at least 4 weeks. Maximum moisture 5%. Seal with |
| Concrete surfaces: sanding, needle gun and mechanical grinding | Closed-circuit blasting, diamond grinding and other suitable methods | |
| and similar, by mechanical treatment | to treat the surrounding concrete surface to remove laitance. | |
| Coated surface | A clean, dry and sound compatible primer. | |
The recommended surface preparation provides optimum properties including adhesion, corrosion resistance, heat resistance and chemical resistance.
This product may be applied by the following methods
| Spray: | Apply by airless spray. |
| Brush: | Recommended for touch-up and small-area application. Take care to achieve the specified dry film thickness. |
| Penguard Pro GF Comp A — General-Purpose Abrasion-Resistant Epoxy Glass Flake, Component A | 3 parts |
| Penguard Pro Comp B Universal Abrasion-resistant Epoxy Mastic, Component B | 1 part |
| Thinner | Jotun Thinner No. 17 |
|---|
| Nozzle tip size (inch/1000): | 21-27 |
| Nozzle pressure (minimum): | 200 bar / 2900 psi |
| Substrate Temperature | 0 °C | 5 °C | 10 °C | 15 °C | 23 °C | 40 °C |
| Touch Dry | 30 h | 15 h | 10 h | 7 h | 3 h | 1 h |
| Walk-on Dry | 55 h | 34 h | 22 h | 16 h | 6 h | 4 h |
| Minimum recoat interval | 45 h | 26 h | 16 h | 12 h | 4 h | 3 h |
| Dry/cured to service | 12 days | 10 days | 7 days | |||
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
Extra care is required when overcoating at low temperatures; the whole coating system requires higher temperatures to cure and develop good mechanical strength.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Induction Time | 10 min |
| Pot Life | 1 h |
Temperature
| Drying, atmospheric | Continuous 120 °C | Peak 140 °C |
| Immersed, sea water | 50 °C | - |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Note: this coating can withstand different immersion temperatures, depending on the specific chemical and whether immersion is continuous or intermittent. Heat resistance is affected by the coating system as a whole. When used with other coatings, ensure that all coatings in the system have similar heat resistance.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Epoxy, modified epoxy, zinc-rich epoxy, zinc silicate, inorganic zinc silicate shop primer |
| Subsequent coat: | Acrylic, epoxy, polyurethane, polysiloxane |
| Volume | Container Size | |
| (L) | ||
| Penguard Pro GF Comp A — General-Purpose Abrasion-Resistant Epoxy Glass Flake, Component A | 15 | 20 |
| Penguard Pro Comp B Universal Abrasion-resistant Epoxy Mastic, Component B | 5 | |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
| Penguard Pro GF Comp A — General-Purpose Abrasion-Resistant Epoxy Glass Flake, Component A | 12 months |
| Penguard Pro Comp B Universal Abrasion-resistant Epoxy Mastic, Component B | 24 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
This product can contribute to green building standard credits. Visit Jotun.com for more information or contact your local JOTUN representative.
EPDs are available at www.epd-norge.no
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.