Jotatemp 1000 Inorganic Ceramic Inert Copolymer Heat-resistant Paint 1000 belongs to heat-resistant paints. It can be used with Jotatemp 540 Zinc primer to provide heat resistance up to 540°C and extend anticorrosive protection. Designed as a heat-resistant coating, it can continuously withstand low temperatures down to -196°C and high temperatures up to 1000°C where the substrate permits. Parameters on this page: volume solids 75 ± 2%, DFT 100–150 µm, theoretical spreading rate 7.5–5 m²/L. Comparable products from the same brand: Aluminium Paint H.R Aluminium Heat-resistant Paint, Chemflake Special Vinyl High-performance Acid-resistant Heat-resistant Paint, Solvalitt 300 Alu Silicone Heat-resistant Aluminium Paint.
Parameter source: JOTUN original technical data sheet (TDS) "Jotatemp 1000 Inorganic Ceramic Inert Copolymer Heat-resistant Paint 1000"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 75 ± 2% |
|---|---|
| Dry Film Thickness | 100–150 µm |
| Theoretical Spreading Rate | 7.5–5 m²/L |
| VOC | 330 g/L (China) |
| Density / Specific Gravity | 1.8 kg/L |
| Number of Components | Three-component |
| Flash Point | 26 °C |
| Thinner | JOTUN Thinner No. 7 / JOTUN Thinner No. 10. To achieve ideal spray performance, the product may be diluted before use… |
| Mixing Ratio | 110 parts : 1 part : 2.5 parts (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Jotatemp 1000
This is a three-component titanium-catalysed inorganic ceramic copolymer coating cured at ambient temperature. It belongs to the polymer coating category. Designed as a heat-resistant coating, it can continuously withstand low temperatures down to -196°C and high temperatures up to 1000°C where the substrate permits. It can be used as a primer or topcoat in atmospheric environments. It is suitable for properly prepared carbon steel and ceramic substrate surfaces. It can be applied to hot substrates at temperatures up to 250°C. Refer to the application instructions for more detailed information. It provides adequate anticorrosive protection at ambient temperature during construction and shutdown periods. This product has passed tests applicable to anticorrosive coatings under insulation.
Industrial protective coatings:
Suitable for carbon steel and ceramic insulated and uninsulated substrate surfaces. For other substrates and temperature ranges, contact the local JOTUN office. Specifically designed to prevent corrosion under insulation (CUI) above 250°C. It can be used with Jotatemp 540 Zinc primer to provide heat resistance up to 540°C and extend anticorrosive protection. For excellent performance on stainless steel and alloy steel (P91) substrates, Jotatemp 1000HT is recommended.
Others
Tested for high durability in corrosivity category C5 according to ISO 12944-6; passed the riser test for CUI performance in ISO 19277-2018.
Passed 1000 h dry heat test at 540°C on carbon steel substrates.
Passed a 1000-hour dry heat test at 1000 °C on ceramic substrates.
Passed ASTM D2485:2018 Standard Test Methods for Evaluating Coatings for High Temperature Service.
Passed ASTM D6944:2009 thermal cycling resistance of cured coatings.
Other certificates and approvals are available on request.
Jotatemp 1000 HT for stainless steel, alloy steel (P91) and ceramic substrates. For different products in this series, refer to their respective technical data sheets.
Dark grey, aluminium, aluminium effect (colour close to RAL 9006)
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 75± 2 % |
| Gloss (GU 60°) | ISO 2813 | Matt (0–35) |
| Flash Point | ISO 3679 Method 1 | 26 °C |
| Density | Theoretical Value | 1.8 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | Calculation | 300 g/L |
| EU | European Paint Directive 2004/42/CE | Calculation | 300 g/L |
| China | GB 30981-2020 Limit of harmful substances of industrial protective coatings | GB/T 23985-2009 8.3 | 330 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 100–150 µm |
| Wet Film Thickness | 130–200 µm |
| Theoretical Spreading Rate | 7.5–5 m²/L |
In a single-coat system, it can be applied up to a dry film thickness of 200 µm.
Surface Preparation
| Substrate | Minimum | Recommended |
| Carbon Steel | St 2 (ISO 8501-1). | Sa 2½ (ISO 8501-1). |
| Ceramic substrates | The surface shall be clean and dry. | |
| Coated surface | A clean, dry and sound compatible primer. | |
This product may be applied by the following methods
| Spray: | Apply by airless spray. |
| Brush: | Recommended for touch-up and small-area application. Take care to achieve the specified dry film thickness. |
| Inorganic Ceramic Inert Copolymer High-temperature Coating 1000, Component A | 110 parts |
| Inorganic Ceramic Inert Copolymer High-temperature Coating 1000, Component B | 1 part |
| Inorganic Ceramic Inert Copolymer High-temperature Coating 1000, Component C | 2.5 parts |
Mix Component A and Component C thoroughly before adding Component B.
| Thinner | JOTUN Thinner No. 7 / JOTUN Thinner No. 10. To achieve ideal spray performance, the product may be diluted at 3–5% by volume before use. |
|---|---|
| Note | Where the Korean VOC regulation (Clean Air Conservation Act) and its corresponding thinning limits differ from the recommended thinning volume, the former prevails. |
In China, the cleaning solvent must comply with GB 38508-2020
| Nozzle tip size (inch/1000): | 17-23 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
| Substrate Temperature | 10 °C | 15 °C | 23 °C | 40 °C | 100 °C |
| Touch Dry | 5.5 h | 3 h | 2.5 h | 1.5 h | 15 min |
| Walk-on Dry | 24 h | 18 h | 6 h | 3.5 h | 15 min |
| Minimum recoat interval | 24 h | 18 h | 6 h | 3.5 h | 0 min |
| Dry/cured to service | 4 days | 3 days | 24 h | 18 h | 15 min |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
As it evaporates rapidly above 100 °C, flash drying may occur.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 10 °C | 15 °C | 23 °C | 40 °C |
| Pot Life | 10 h | 8 h | 6 h | 4 h |
Carbon steel:
| Continuous | 540°C |
|---|
Ceramic substrates:
| Continuous | 1000°C |
|---|
The continuous service temperature limit is based on the heat resistance of the substrate.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Zinc silicate, inert copolymer matrix, itself |
| Subsequent coat: | Silicone acrylic |
| Volume | Container Size | |
| (L) | ||
| Inorganic Ceramic Inert Copolymer High-temperature Coating 1000, Component A | 4.4 | 5 |
| Inorganic Ceramic Inert Copolymer High-temperature Coating 1000, Component B | 0.04 | 0.25 |
| Inorganic Ceramic Inert Copolymer High-temperature Coating 1000, Component C | 0.1 | 1 |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
Storage temperature shall not exceed 40 °C.
| Inorganic Ceramic Inert Copolymer High-temperature Coating 1000, Component A | 12 months |
| Inorganic Ceramic Inert Copolymer High-temperature Coating 1000, Component B | 24 months |
| Inorganic Ceramic Inert Copolymer High-temperature Coating 1000, Component C | 24 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.