Hardtop Peelable TU Waterborne Peelable Protective Topcoat TU is a waterborne coating used as a topcoat. It is used for temporary protection of the final coat of a complete coating system, protecting against dust, oil, grease, flash rust and overspray. It is a one-component physically drying waterborne coating used for temporary protection against various contaminants and light mechanical wear. Parameters on this page: volume solids 44 ± 2%, dry film thickness 125-250 µm, theoretical spreading rate 3.5-1.8 m²/L. Comparable models from the same brand: Hardtop Peelable Waterborne Peelable Protective Topcoat, Hardtop Clear WF waterborne polyurethane clearcoat, Hardtop E99 WF HG waterborne polyurethane high-gloss topcoat HG.
Parameter source: JOTUN original technical data sheet (TDS) for Hardtop Peelable TU Waterborne Peelable Protective Topcoat TU; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 44 ± 2% |
|---|---|
| Dry Film Thickness | 125–250 µm |
| Theoretical Spreading Rate | 3.5–1.8 m²/L |
| VOC | GB/T 23985-2009 8.4, 95 g/L (China) |
| Density / Specific Gravity | 1.1 kg/L |
| Number of Components | One-component |
| Gloss | Matt (0–35) |
| Wet Film Thickness | 285–570 µm |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Hardtop Peelable TU
A one-component physically drying waterborne coating used for temporary protection against various contaminants and light mechanical wear. Its film has a matt effect. It has good resistance to weld spatter and flame spread, and can dry at temperatures as low as 5 °C. It is suitable for coated substrates. After a period of external exposure, it has good peelability. Designed specifically for touch-up application.
Used as temporary protection of the final coat of a complete coating system, preventing dust, oil, grease, flash rust and overspray.
Others
Hardtop Peelable Waterborne Peelable Protective Topcoat. For the different products in this series, refer to the respective technical data sheets.
Pink
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 44± 2 % |
| Gloss (GU 60°) | ISO 2813 | Matt (0–35) |
| Density | Theoretical Value | 1.1 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | Calculation | 52 g/L |
| Hong Kong | Air Pollution Control (VOC) Regulation | Calculation | 52 g/L |
| EU | European Paint Directive 2004/42/CE | Calculation | 23 g/L |
| China | GB 30981-2020 Limit of harmful substances of industrial protective coatings | GB/T 23985-2009 8.4, 95 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 125–250 µm |
| Wet Film Thickness | 285–570 µm |
| Theoretical Spreading Rate | 3.5–1.8 m²/L |
When the applied film thickness is lower than specified, the strippability may be affected. Achieving the recommended dry film thickness is important.
For good results, the substrate shall be clean and free from other contaminants.
It is strongly recommended to prepare a representative small area before applying over a large area, to ensure compatibility with the substrate and that stripping is possible, and to achieve the performance over the temporary protection period. Overcoated surfaces: it is important that after overcoating the coating is fully cured and that the gloss and colour also perform well. This is particularly important for durable decorative topcoats, to confirm they are not affected by the application of the strippable coating.
For details, consult your local JOTUN office.
This product may be applied by the following methods
| Brush: | Recommended for small-area application. Ensure that the specified dry film thickness is achieved. |
| Roller: | Roller application is recommended; ensure that the specified dry film thickness is achieved. |
For spray application, Hardtop Peelable is recommended.
One-component
Do not add thinner.
| Cleaner | Water |
|---|
| Substrate Temperature | 5 °C | 10 °C | 23 °C | 40 °C |
| Touch Dry | 30 min | 25 min | 10 min | |
| Walk-on Dry | 100 min | 80 min | 60 min | 30 min |
| Minimum recoat interval | * | |||
| Maximum recoat interval after drying, atmospheric environment | Unlimited | |||
For minimum and maximum overcoating intervals, refer to the Application Guide (AG) of this product.
* Recoat after drying, minimum interval, in atmosphere — for more information, see the Application Guide.
This product may be used only on a complete coating system.
Freshly applied coatings shall not be exposed to rain or water until after 24 hours.
Drying time depends on the degree of ventilation. Poorer ventilation leads to longer drying times.
| Minimum stripping time | 23 °C: 1 h |
|---|
This is the minimum time before large areas of the coating can be stripped by hand.
The maximum waiting time before stripping depends on the actual film thickness, exposure conditions and exposure time. Test areas shall be prepared to periodically check that stripping is still easy.
Drying and curing times are determined based on temperature and relative humidity below 75%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Maximum recoat interval after drying, atmospheric environment: the maximum time interval before the next coat may be applied without any surface preparation.
Temperature
| Continuous | Peak | |
| Drying, atmospheric | 60 °C | - |
At elevated temperatures, the dry film gradually softens. Establish correct handling and stacking procedures according to the environmental conditions. Protective performance is unaffected.
Previous coat:
Jotacote Universal N10 universal abrasion-resistant epoxy N10 (0B9) Penguard Universal reinforced universal abrasion-resistant epoxy (0R5) Penguard HB II epoxy high-build topcoat II (0RU) Jotacote F60 epoxy F60 (5CJ) Epoxy HR phenolic epoxy heat-resistant coating (0ST) Jotatemp 250 glass flake reinforced phenolic epoxy heat-resistant coating (0Y6) Jotaprime 500 epoxy primer 500 (0AZ) Penguard FC epoxy FC (0UW) Jotamastic 90 low surface treatment epoxy abrasion-resistant coating 90 (0D5) Hardtop AX aliphatic polyurethane topcoat AX (0D3) Hardtop WT8 high-performance polyurethane topcoat WT8 (6FN) Hardtop AX K aliphatic polyurethane topcoat AX K (5FK) Hardtop AX K II aliphatic polyurethane topcoat AX K II (0XH) Megagloss AC Megagloss HG. For surfaces of other products not mentioned above, consult JOTUN before applying Waterborne Peelable Protective Topcoat and Waterborne Peelable Protective Topcoat TU.
| Subsequent coat: | itself and Hardtop Peelable Waterborne Peelable Protective Topcoat |
|---|
| Volume | Container Size | |
| (L) | ||
| Waterborne Peelable Protective Topcoat TU | 5 | |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
To prevent freezing, the storage temperature shall be above 5 °C
Waterborne Peelable Protective Topcoat TU 12 months
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.