Hardtop Metallic Uni WF Water-borne Polyurethane Metallic Topcoat is a water-borne paint used as a topcoat. Industrial protective coatings segment: suitable for a range of steel structures exposed to various corrosive environments. Used as part of a complete water-borne system over JOTUN-recommended water-borne primers, or as part of a mixed system over suitable solvent-borne primers. Parameters on this page: volume solids 38 ± 2%, dry film thickness 40–60 µm, theoretical spreading rate 9.5–6.3 m²/L. Comparable models from the same brand: Hardtop Clear WF Water-borne Polyurethane Clearcoat, Hardtop E99 WF HG Water-borne Polyurethane High-gloss Topcoat HG, Hardtop E99 WF Water-borne Polyurethane High-gloss Topcoat.
Parameter source: JOTUN original technical data sheet (TDS) "Hardtop Metallic Uni WF Water-borne Polyurethane Metallic Topcoat"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 38 ± 2% |
|---|---|
| Dry Film Thickness | 40–60 µm |
| Theoretical Spreading Rate | 9.5–6.3 m²/L |
| VOC | 207 g/L (China) |
| Density / Specific Gravity | 1.04 kg/L |
| Number of Components | Two-component |
| Flash Point | 100 °C |
| Thinner | Deionised water |
| Mixing Ratio | 8 parts : 1 part (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Hardtop Metallic Uni WF
This is a water-borne two-component chemically curing aliphatic acrylic polyurethane coating. A range of metallic topcoats with excellent gloss retention is available. The product contains aluminium pigment. The product provides a uniform appearance and good application properties. It is a general-purpose outdoor product. Used as part of a complete water-borne system over JOTUN-recommended water-borne primers, or as part of a mixed system over suitable solvent-borne primers.
Industrial protective coatings:
Suitable for a range of steel structures exposed to various corrosive environments. Recommended for refineries, power stations, bridges, buildings and general equipment. Widely applicable to industrial buildings.
Others
Selected metallic colours preferred.
| Note | The colour of the previous coat affects the appearance and colour of the metallic topcoat. |
|---|
To achieve the closest match to the colour card, the recommended primer colours shall be used for the previous coat:
Light aluminium 9006, aluminium grey 9007, MIO 701, MIO 703: light grey; champagne gold, Maillard brown: light yellow or grey XO. Different application methods, dry film thicknesses, temperatures, humidity and substrates will produce different results.
Due to technical limitations, exact matching of metallic topcoat colours is not possible
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 38± 2 % |
| Flash Point | ISO 3679 Method 1 | 100 °C |
| Density | Theoretical Value | 1.04 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| China | GB 30981-2020 Limit of harmful substances of industrial protective coatings | GB/T 23986-2009 10.4 | 207 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
All data apply to the mixed paint only.
Typical recommended specification range
| Dry Film Thickness | 40–60 µm |
| Wet Film Thickness | 100–160 µm |
| Theoretical Spreading Rate | 9.5–6.3 m²/L |
Bright colours may require a higher dry film thickness within the recommended range to achieve hiding.
To ensure long-term adhesion of the subsequent coat, all surfaces must be clean, dry and free from contaminants. Direct application of this product to carbon steel substrates is not recommended.
Surface Preparation
| Substrate | Minimum | Recommended |
| Coated surface | A clean, dry and sound compatible primer. | |
This product may be applied by the following methods
| Spray | Apply by air spray or airless spray. |
|---|
Different application methods or techniques may produce different metallic effects. For more details, refer to the Application Guide or other JOTUN documents.
| Hardtop Metallic UNI WF Comp A | 8 parts |
| Hardtop Metallic UNI WF Comp B | 1 part |
The paint shall be stirred with clean, suitable mechanical stirring tools. Stir Component A thoroughly before adding any Component B or thinner. Add Component B before adding any thinner, and stir Components A and B thoroughly with a stirring tool.
| Thinner | Deionised water |
|---|
Different thinning ratios may give different colours, and an excessively high thinner ratio may affect the uniformity of the coating.
Metal ions in tap water may cause early failure of corrosion protection. If thinning is required, up to 35% water may be added for air spray and up to 5% water for airless spray; addition shall be carried out after the two components have been mixed.
| Nozzle tip size (inch/1000): | 11-15 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
For further information, see the Application Guide.
| Nozzle tip size: | 13–15 (inch/1000) / pressure pot: 1.3–1.5 (mm) |
| Nozzle pressure (minimum): | 2.1 bar/30 psi / pressure pot: 2.1 bar/30 psi |
Fluctuations in gun tip pressure may affect the orientation of aluminium flakes and the brightness of the film.
| Substrate Temperature | 10 °C | 23 °C | 35 °C |
| Touch Dry | 1 h | 30 min | 20 min |
| Walk-on Dry | 24 h | 5.5 h | 2 h |
| Minimum recoat interval | 24 h | 5.5 h | 2 h |
| Dry/cured to service | 15 days | 7 days | 3 days |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 80%, with dry film thickness within the average range.
After flash-off, the product may be force dried at a maximum of 60°C.
| Walk-on Dry | 1 h |
|---|
Minimum flash-off time at the substrate temperature.
10°C: 1 h
23°C: 45 min
35°C: 30 min
The minimum flash-off time is the minimum waiting time before force drying to allow moisture to evaporate.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Pot Life | 3 h |
Temperature
| Continuous | Peak | |
| Drying, atmospheric | 120°C | 140 °C |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Epoxy, modified epoxy |
| Subsequent coat: | Polyurethane |
Other information
Preparation and cleaning of application equipment. To avoid contamination of water-borne paint by solvent, spray equipment must be cleaned before use. All equipment containing solvent, such as pumps, lines and guns, must be thoroughly cleaned in accordance with the following instructions.
If the application equipment is stainless steel, designed for and used only with water-borne coatings, this preparation and cleaning procedure is not required.
Before spraying:
Flush equipment and lines with JOTUN Thinner No. 17, then with Thinner No. 4, and finally with fresh water.
After spraying:
Clean equipment and lines with water and an alkaline degreaser, then flush with JOTUN Thinner No. 4, and finally with JOTUN Thinner No. 17.
| Volume | Container Size | |
| (L) | ||
| Hardtop Metallic UNI WF Comp A | 16.8 | 20 |
| Hardtop Metallic UNI WF Comp B | 2.1 | 2.2 |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
Protect from frost during transport and storage. Recommended storage temperature 5 °C to 35 °C.
| Hardtop Metallic UNI WF Comp A | 12 months |
| Hardtop Metallic UNI WF Comp B | 24 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.