Barrier 75 CN Epoxy Zinc-rich Primer belongs to zinc-rich primers, epoxy coating system. Industrial protective coatings field: suitable for steel structures and pipelines under corrosivity category C5 (ISO 12944-2) and below. Suitable for properly prepared carbon steel, repair of inorganic zinc silicate coatings and worn galvanized steel surfaces. Parameters on this page: volume solids 66 ± 2%, dry film thickness 60–100 µm, theoretical spreading rate 11.1–6.7 m²/L. Comparable products of the same brand and type: Barrier 65 S Epoxy Zinc-rich Primer, Barrier 65 Epoxy Zinc-rich Primer, Barrier 77 Epoxy Zinc-rich Primer.
Parameter source: JOTUN original technical data sheet (TDS) 'Barrier 75 CN Epoxy Zinc-rich Primer'; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 66 ± 2% |
|---|---|
| Dry Film Thickness | 60–100 µm |
| Theoretical Spreading Rate | 11.1–6.7 m²/L |
| VOC | 306 g/L (China) |
| Density / Specific Gravity | 2 kg/L |
| Number of Components | Two-component |
| Flash Point | 25 °C |
| Thinner | Jotun Thinner No. 69 |
| Mixing Ratio | 4 parts : 1 part (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Barrier 75 CN
This is a two-component polyamine-cured zinc-rich epoxy coating. It is a fast-drying, high-zinc-content product. It complies with the requirements of Grade 2 of the Chinese standard HG/T 3668-2009 for zinc dust specifications.
Provides good anticorrosive performance when used in coating systems with other paints. Used as a primer in atmospheric environments. Suitable for properly prepared carbon steel, repair of inorganic zinc silicate coatings and worn galvanized steel surfaces. It can be applied at substrate temperatures below zero. The zinc dust in this product complies with ASTM D520, Type II.
Industrial protective coatings:
Suitable for steel structures and pipes in corrosivity categories up to C5 (ISO 12944-2). Recommended for offshore environments such as refineries, power stations, bridges, buildings, mining equipment and general structural steel. Designed as a primer in coating systems requiring better durability.
Others
Grey
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 66± 2 % |
| Gloss (GU 60°) | ISO 2813 | Matt (0–35) |
| Flash Point | ISO 3679 Method 1 | 25 °C |
| Density | Theoretical Value | 2 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| China | Mandatory national standard of China | GB 30981.2-2025 | 306 g/L |
| Coating hazards GB | 30981.2-S-Pb≤1000-NC |
Contains reactive thinner
The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 60–100 µm |
| Wet Film Thickness | 90–150 µm |
| Theoretical Spreading Rate | 11.1–6.7 m²/L |
Surface Preparation
| Substrate | Minimum | Recommended |
| Carbon Steel | St 3 (ISO 8501-1) | Sa 2½ (ISO 8501-1) |
| Shop-primed Steel | Clean, dry, intact and approved shop primer (compliant | Sweep blast or abrasive blast clean at least 70% of the area to Sa |
| compliant with ISO 12944-4 clause 5.4). | 2 (ISO 8501-1) |
This product may be applied by the following methods
| Spray: | Apply by air spray or airless spray. |
| Brush: | Recommended for touch-up and small-area application. Take care to achieve the specified dry film thickness. |
| Barrier 75 CN Comp A — Epoxy Zinc-Rich Primer 0X6, Component A | 4 parts |
| Barrier 75 CN Comp B — Epoxy Zinc-Rich Primer 0X6, Component B | 1 part |
| Thinner: | Jotun Thinner No. 17 | /Jotun Thinner No. 69 |
| JOTUN Thinner No. 17 | JOTUN Thinner No. 69 (092) |
Jotun Thinner No. 17: to accelerate evaporation. Jotun Thinner No. 69 (092): to retard evaporation, max 10%.
When the air temperature exceeds 30 °C, JOTUN Thinner No. 69 is recommended.
If the relative humidity is below 30% and the air temperature exceeds 25 °C, JOTUN Thinner No. 69 is recommended.
| Nozzle tip size (inch/1000): | 15-21 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
| Substrate Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 23 °C | 40 °C |
| Touch Dry | 2 h | 1 h | 40 min | 20 min | 6 min | 3 min |
| Walk-on Dry | 24 h | 10 h | 5 h | 2 h | 1 h | 30 min |
| Minimum recoat interval | 24 h | 10 h | 5 h | 2 h | 1 h | 30 min |
| Dry/cured to service | 20 days | 14 days | 10 days | 7 days | 5 days | 2 days |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Pot Life | 2 h |
| Pot life is affected by temperature and humidity up to 85%. |
Temperature
| Continuous | Peak | |
| Drying, atmospheric | 120°C | 140 °C |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Inorganic zinc shop primer |
| Subsequent coat: | Epoxy, modified epoxy, polyurethane |
| Volume | Container Size | |
| (L) | ||
| Barrier 75 CN Comp A — Epoxy Zinc-Rich Primer 0X6, Component A | 7.2 | 10 |
| Barrier 75 CN Comp B — Epoxy Zinc-Rich Primer 0X6, Component B | 1.8 | 3 |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
| Barrier 75 CN Comp A — Epoxy Zinc-Rich Primer 0X6, Component A | 24 months |
| Barrier 75 CN Comp B — Epoxy Zinc-Rich Primer 0X6, Component B | 24 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.