Baltoflake Ecolife Glass-flake-reinforced Unsaturated Polyester Coating is a glass flake coating. Recommended for areas frequently subjected to mechanical abrasion and exposed to harsh environments. Suitable for suitably prepared carbon steel, stainless steel, aluminium and approved primers; can be applied at surface temperatures down to 5 °C. Parameters on this page: volume solids 93 ± 2%; dry film thickness 600–1500 µm; theoretical spreading rate 1.54–0.62 m²/L. Comparable products from the same brand: Chemtech GM Two-component Solvent-free Polyamine-cured Epoxy Coating, Jotaguard 100 Two-component Solvent-free Polyamine-cured Epoxy Coating, Jotamastic Plus Amine-cured Low Surface Treatment Epoxy Coating.
Source: JOTUN original technical data sheet (TDS) 'Baltoflake Ecolife Glass-flake-reinforced Unsaturated Polyester Coating'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 93 ± 2% |
|---|---|
| Dry Film Thickness | 600–1500 µm |
| Theoretical Spreading Rate | 1.54–0.62 m²/L |
| VOC | 39 g/L (EU IED) |
| Density / Specific Gravity | 1.2 kg/L * |
| Number of Components | Two-component |
| Flash Point | 53 °C |
| Gloss | Matt (0–35) |
| Wet Film Thickness | 650–1610 µm |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Baltoflake Ecolife
A styrene-free, glass-flake-reinforced unsaturated polyester coating. An ultra-high-build protective coating with high abrasion resistance and fast curing. Can be used as a primer, intermediate coat or topcoat in atmospheric and immersed environments. Suitable for suitably prepared carbon steel, stainless steel, aluminium and approved primers; can be applied at surface temperatures down to 5 °C.
Recommended for areas subject to frequent mechanical abrasion and severe service environments. Recommended for offshore environments, including splash zones, breakwaters, piles, tidal zones, decks, battery rooms, power stations, exteriors of buried tanks, concrete embankments, refineries, bridges, mining equipment and general structural steel that is difficult to maintain.
Others
Pre-qualified in the selected coating system in accordance with NORSOK M-501; certified compliant with the low flame-spread requirements of the IMO 2010 FTP Code. For details, consult your JOTUN representative.
Other certificates and approvals are available on request.
Many other colours are available
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 93± 2 % |
| Weight solids | 98 ± 2 % | |
| Gloss (GU 60°) | ISO 2813 | Matt (0–35) |
| Flash Point | ISO 3679 Method 1 | 53 °C |
| Density | Theoretical Value | 1.2 kg/L * |
| Region | Regulations | Test / Standard | VOC Value |
| EU IED | Industrial Emission Directive 2010/75/EU | ISO 3233 | 39 g/L |
| EU IED | ISO 3233 | 56 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
*VOC information: theoretically, under ideal conditions, unsaturated polyester products volatilize no reactive monomers or other components during curing. This means the material applied to the surface remains in the coating after curing. In practice, a small amount of monomer (vinyl toluene) may volatilize during application and curing. Based on the theory that all reactive monomers react into the matrix, the theoretical VOC content calculated per the EU Industrial Emissions Directive 2010/75/EU is 17 g/L.
*/**/*** See the comments below.
* The ideal method for VOC measurement of this type of product is to follow the test standard ISO 3233.
** At 23 °C, 750 µm wet film thickness and 2.5% (by volume) peroxide addition, the measured VOC content is 39 g/L.
*** At 23 °C, 750 µm wet film thickness and 1.25% (by volume) peroxide addition, the measured VOC content is 56 g/L.
Typical recommended specification range
| Dry Film Thickness | 600–1500 µm |
| Wet Film Thickness | 650–1610 µm |
| Theoretical Spreading Rate | 1.54–0.62 m²/L |
All vinyl ester and polyester coatings may shrink during curing. This makes the practical spreading rate lower than the theoretical. The shrinkage depends on the actual dry film thickness and application conditions.
Surface Preparation
| Substrate | Minimum | Recommended |
| Carbon Steel | Sa 2½ (ISO 8501-1); surface roughness medium to coarse G (ISO 8503-2) | |
| Stainless steel | Cleanliness to Sa 2½ (ISO 8501-1), with a fine to medium G surface roughness (ISO 8503-2). | |
| Aluminium | Cleanliness and surface roughness per Sa 2½ (ISO 8501-1) and medium to coarse G (ISO 8503-2) respectively | |
| Coated surface | A clean, dry and sound compatible primer. | |
This product may be applied by the following methods
| Spray: | Standard airless spray may be used. Dedicated two-component airless spray is optional. |
| Brush: | Recommended for touch-up and small-area application. Take care to achieve the specified dry film thickness. |
The substrate temperature must not be below the paint temperature, nor more than 20 °C above it.
Additive addition per 16 L of product (ml).
Due to differing regional regulations, packaging sizes and fill capacities may vary by region. Adjust the quantity of additive accordingly.
Paint temperature
| Additives | 5-9 °C | 10-14 °C | 15-19 °C | 20-24 °C | 25-29 °C | 30-34 °C |
| Jotun Inhibitor 53 or Inhibitor NLC-10 | 15 | 30 | 40 | 50 | 60 | |
| Jotun Peroxide 13, Norox KPM or Trigonox 61 | 400 | 200 | 200 | 200 |
For plural two-component airless spray pumps:
The recommended peroxide (Jotun Peroxide 13, Norox KPM or Trigonox 61) addition for substrate temperature is as follows:
| Temperature: | Addition: |
| 5-9°C: | 2.5% (by volume) |
| 10-40°C: | 1.25% (by volume) |
In special cases, if faster curing is required, or equipment limitations require more peroxide even at substrate temperatures above 10 °C, a higher addition may be used provided the shortened overcoating time is acceptable.
It is recommended to mix the product and hardener at 18 °C or above. The stated pot life is for 1.25% (by volume) peroxide addition at 23 °C. When using a two-component spray pump, to better control the time before gelling in the pump and hoses, maintain the temperature close to 23 °C with a maximum deviation of +/- 5 °C (i.e. 18–28 °C).
| Warning | The accelerator must never come into direct contact with peroxides. |
|---|
All peroxides must be stored in a dark, cool environment (below 25 °C), away from all flammable materials. Do not expose to direct sunlight. Use only original or approved containers.
Empty containers should be rinsed with water and stored separately.
Peroxides ignite if exposed to sparks and hot metal dust from grinding or other mechanical work.
The curing reaction generates heat. Fill containers of surplus mixed paint with water to avoid excessive heat build-up.
| Thinner: | Vinyl toluene |
| Cleaner: | Jotun Thinner No. 17 / Jotun Thinner No. 27 |
Thinning of this product is not recommended.
When the thinner is used as a cleaning solvent, it must first comply with local regulatory requirements
| Nozzle tip size (inch/1000): | 27-35 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
| Substrate Temperature | 5 °C | 10 °C | 15 °C | 19 °C | 23 °C | 30 °C | 40 °C |
| Use two-component airless spray | |||||||
|---|---|---|---|---|---|---|---|
| Touch Dry | 2.5 h | 2 h | 1 h | 45 min | |||
| Walk-on Dry | 2.5 h | 2 h | 1 h | 45 min | |||
| Minimum recoat interval | 2.5 h | 2 h | 1 h | 45 min | |||
| Dry/cured to service | 3 days | 2 days | 12 h | 4 h | |||
| Use one-component airless spray; touch dry | 3 h | 2.5 h | 2 h | 2 h | |||
| Walk-on Dry | 3 h | 2.5 h | 2 h | 2 h | |||
| Minimum recoat interval | 3 h | 2.5 h | 2 h | ||||
| Dry/cured to service | 3 days | 2 days | 1 day | 1 day | |||
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Pot Life | 15–20 min |
The stated pot life is for 1.25% (by volume) peroxide addition at 23 °C; at higher temperatures the pot life is shortened.
For one-component ordinary airless spray, the pot life after adding the inhibitor per the mixing table: 35 minutes.
Temperature
| Drying, atmospheric | Continuous 90 °C | Peak 100 °C |
| Immersed, sea water | 50 °C | |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Note: this coating can withstand different immersion temperatures, depending on the specific chemical and whether immersion is continuous or intermittent. Heat resistance is affected by the coating system as a whole. When used with other coatings, ensure that all coatings in the system have similar heat resistance.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Unsaturated polyester |
| Subsequent coat: | Unsaturated polyester, polyurethane, polysiloxane |
| Volume | Container Size | |
| (L) | ||
| Baltoflake Ecolife Glass Flake Polyester Paint (styrene-free) | 16 | 20 |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
Storage temperature not exceeding 25 °C.
Baltoflake Ecolife, 6 months, Glass Flake Polyester Paint (styrene-free)
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
This product can contribute to green building standard credits. Visit Jotun.com for more information or contact your local JOTUN representative.
EPDs are available at www.epd-norge.no
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.