Intercure 200 Fast-drying Epoxy Primer is an epoxy coating used as a primer. Under most climatic conditions, it is suitable for recoating within 3 h, accelerating production and increasing the output of fabrication shops. A two-component zinc phosphate/micaceous iron oxide epoxy primer formulated with unique polymer technology, it can cure and be recoated rapidly even at low temperatures. Although low-molecular-weight reactive additives become part of the film upon curing under normal ambient conditions, analysis by EPA Method 24 shows that they also affect the VOC value. Parameters on this page: dry film thickness 75–100 µm (3–4 mil), theoretical spreading rate 8.93 m²/L, number of components: two.
Parameter source: AKZONOBEL manufacturer's Technical Data Sheet (TDS) "Intercure 200 Fast-drying Epoxy Primer"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 67% |
|---|---|
| Dry Film Thickness | 75–100 µm (3–4 mils) |
| Theoretical Spreading Rate | 8.93 m²/L |
| VOC | 2.67 lb/gal (320 g/L) US Environmental Protection Agency Method 24 213… |
| Density / Specific Gravity | 1.6 kg/L (13.4 lb/gal) |
| Number of Components | Two-component |
| Thinner | Normally no thinning is required |
| Mixing Ratio | 3 parts : 1 part (by volume) |
| Colour / Appearance | Available in a limited range of colours, INTERCURE 200 |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
A two-component epoxy zinc phosphate/micaceous iron oxide primer formulated with unique polymer technology that cures and overcoats rapidly even at low temperatures.
A high-solids product with a low volatile organic compound (VOC) content.
Suitable for overcoating within 3 hours in most climates, thereby accelerating production and increasing throughput at fabrication shops.
Also suitable for use on site as a fast-curing maintenance coating.
| Colour | Available in a limited range of colours, INTERCURE 200 |
|---|---|
| Gloss | Matt |
| Volume Solids | 67% |
| Typical thickness | DFT 75–100 µm (3–4 mil) corresponds to WFT 112–149 µm (4.5–6 mil) |
| Theoretical Spreading Rate | At 75 µm dry film thickness and the stated volume solids: 8.93 m²/L; at 3 mils dry film thickness and the stated volume solids: 358 ft²/US gal |
| Practical Spreading Rate | Allowing for a suitable loss factor |
| Application Methods | Suitable for airless spray, air spray, brush, roller. Drying time; recommended topcoat recoat interval |
| Temperature | Surface Dry | Hard Dry | Minimum | Maximum |
| 5°C (41°F) | 40 min | 4.5 h | 3 h | Unlimited¹ |
| 15°C (59°F) | 30 min | 3 h | 2 h | Unlimited¹ |
| 25°C (77°F) | 20 min | 2 h | 1 h | Unlimited¹ |
| 40°C (104°F) | 15 min | 30 min | Unlimited¹ | |
¹ See Definitions and Abbreviations from the International Paint Protective Coatings division. When polysiloxane topcoats are used, the maximum recoat interval is reduced. For details, consult International Paint.
| Flash point (typical) | Component A 27 °C (81 °F); Component B 28 °C (82 °F); mixed 27 °C (81 °F) |
|---|---|
| Product weight | 1.6 kg/L (13.4 lb/gal) |
| Volatile Organic Compounds | 2.67 lb/gal (320 g/L) US Environmental Protection Agency Method 24 213 g/kg European Community Solvent Emissions Directive content (EU Council Directive 2010/75/EU) 297 g/L China National Standard GB 23985 coating hazard GB 30981.2-S-Pb≤1000-NC complies with GB 30981.2-2025. For more detailed information, see the section on "Product Characteristics". |
All surfaces to be coated must be clean, dry and free of contaminants. Before application, all surfaces must be assessed and prepared in accordance with ISO 8504:2019.
Oil and grease must be removed in accordance with the SSPC-SP1 solvent cleaning standard.
Abrasive blast cleaning with steel grit to Sa2½ (ISO 8501-1:2007) or SSPC-SP6. If oxidation occurs between abrasive blast cleaning and application of Intercure 200, the surface shall be re-blast cleaned to the specified visual standard.
Surface defects exposed by blast cleaning must be ground, filled or treated by a suitable method.
A sharp, angular surface profile of 50–75 µm (2–3 mil) is recommended.
Intercure 200 is suitable for surfaces that initially meet the above standard by abrasive blast cleaning and then naturally degrade for no more than 7–10 days under good shop conditions. The surface may degrade to Sa2, but there must be no loose powdery rust.
Welds and damaged areas of shop-primed steel structures shall be blast-cleaned with steel grit to Sa2½ (ISO 8501-1:2007) or SSPC SP6.
If the shop primer shows extensive or scattered breakdown, a full sweep blast may be required.
If shop primer is applied over a shot-blasted surface, full sweep blasting with steel grit is required before application of Intercure 200.
| Mixing | This product is supplied in two containers forming one unit. Mix the two components in the specified ratio in one operation. Once mixed, use within the specified pot life. |
|---|
(1) Stir the base (Component A) with a power mixer.
(2) Mix all of the curing agent (Component B) with the base (Component A) and stir thoroughly with a power mixer.
| Mixing ratio | 3 parts : 1 part (by volume) |
|---|
| Pot life | 5°C (41°F) | 15°C (59°F) | 25°C (77°F) | 40°C (104°F) |
| 6 h | 3 h | 2 h | 45 min |
| Suitable for airless spray | Recommended: nozzle diameter 0.43–0.53 mm (17–21 thousandths of an inch); total paint pressure at the nozzle not less than 176 kg/cm² (2503 psi) |
|---|
| Air Spray | Recommended | Spray gun | DeVilbiss MBC or JGA |
| Air nozzle | 704 or 765 | ||
| (with pressure pot) | Nozzle | E | |
| Brush | Applicable — for small-area repair only | Typical thickness 50–75 µm (2.0–3.0 mils) | |
| Roller application | Applicable — for small-area repair only | Typical thickness 50–75 µm (2.0–3.0 mils) | |
| Thinner | International GTA220 (or | Normally no thinning is required. |
or International GTA415). In extreme cases, consult the local technical representative.
Do not thin beyond the requirements of local environmental regulations.
| Cleaner | International GTA220 (or International GTA415) |
|---|---|
| Interruption of work | Do not leave paint in hoses, spray guns or spray equipment. Flush all equipment thoroughly with International thinner. |
Once mixed, paint should not be resealed. If work is interrupted for too long, mix a fresh batch for application.
| Cleaning | All equipment should be cleaned immediately after use with International thinner. Flushing spray equipment periodically during daily work is good practice. Cleaning frequency depends on the volume sprayed, temperature, spraying time, including interruptions, and other factors. |
|---|
All surplus paint and empty containers must be disposed of in accordance with the relevant local laws/regulations.
Intercure 200 is suitable for use with some products in certain chemical environments, because zinc-containing coatings are attacked by acids and alkalis in such environments.
The maximum recoat interval depends on the integrity of the exposed film. A film at 75 µm (3 mils) dry film thickness can generally be recoated after 6 months of exposure, after suitable cleaning and repair of any damaged areas.
Avoid excessive film thickness, since the adhesion of a topcoat over an aged thick film is not as good as over a film at the specified thickness. When used as a holding primer, avoid excessive film thickness, since intercoat adhesion problems can arise if the subsequent coat is also applied too thickly.
The temperature of the surface to be coated must be at least 3 °C (5 °F) above the dew point.
This product must be thinned only with the recommended International thinner. Other thinners, especially those containing ketones, severely inhibit the curing of the coating.
Intercure 200 can cure below 0°C (32°F). However, the product should not be applied at 0°C (32°F), because ice may form on the substrate.
For details of curing times and recoatability, contact International Paint.
Due to relatively rapid fading, the product is not available in light and coloured shades. In addition, like all epoxy resin coatings, Intercure 200 will chalk under outdoor exposure. However, these phenomena do not adversely affect corrosion protection performance.
In C1 and C2 corrosion environments (ISO 12944), welds and damaged areas may be cleaned by hand or power tool. For more information, consult International Paint Protective Coatings.
Intercure 200 is not suitable for steel structures that may be immersed in water.
In addition to abrasive blast cleaned surfaces, Intercure 200 can be used on other substrates, such as stainless steel and alloys. Contact International Paint Industrial Coatings for details.
Intercoat adhesion when applied over aged Intercure 200 is somewhat lower than when applied over a new coating, but it still meets the requirements of the specified use.
Note: the VOC value given is based on the maximum possible value for the product and may vary with colour and general production tolerances.
Although the low-molecular-weight reactive additive becomes part of the film when cured under normal ambient conditions, analysis by EPA Method 24 shows that it also affects the VOC value.
Intercure 200 is typically applied to suitably prepared steel, such as abrasive blast cleaned steel. However, if required, it can also be applied over a blast-cleaned pre-treatment primer. Consult International Paint Industrial Coatings for specific details.
The following primers may be used with Intercure 200:
| Interzinc 22 | *(A mist coat or tie coat may be required) The following topcoats/intermediate coats are recommended for Intercure 200: |
|---|---|
| Intercure 420 | Interthane 990 |
| Interfine 979 | Interthane 990E |
| Intergard 475HS | Interzone 1000 |
| Intergard 740 | Interzone 954Interseal 670HS For other suitable topcoats/intermediate coats, consult International Paint Industrial Coatings. |
For details, see the relevant product data sheet
| For further information on the industry standards, terms and abbreviations used in this datasheet, see www.international-pc.com | In the following documents on the website: • Definitions and abbreviations • Surface preparation • Coating application • Theoretical and practical spreading rate. These sections are also available as separate publications on request. |
|---|
This product must be applied at the production site by professional applicators in accordance with the recommendations in this manual, the Material Safety Data Sheet and the instructions on the container label. Do not use this product without first reviewing the Material Safety Data Sheet (MSDS) that International Paint provides for its customers.
All work related to the application and use of this product must be carried out in accordance with the relevant national health, safety and environmental standards and regulations.
If welding or flame cutting is required on metal coated with this product, dust and fumes will be generated; use appropriate personal protective equipment and adequate local ventilation.
If in doubt about the suitability of this product for the intended use, consult AkzoNobel for further advice.
| Packaging Specifications | Component A | Component B | ||
| Volume | Packaging | Volume | Packaging | |
| 20 L | 15 L | 20 L | 5 L | |
| 4 US gal | 3 US gal | 5 US gal | 1 US gal | |
For other packaging sizes, contact AkzoNobel.
| Packaging Specifications | Component A | Component B |
| 20 L | 29.1 kg | 5.3 kg |
| 4 US gal | 49.8 lb | 8.8 lb |
| Shelf life | At least 12 months at 25 °C (77 °F). Thereafter, inspection is required. Store in a dry, cool environment away from heat and sources of ignition. |
|---|
© 2026/5/26 AkzoNobel. All rights reserved.
All registered trademarks mentioned in this publication are licensed to or owned by AkzoNobel.
www.international-pc.com
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.
The factory product codes of Intercure 200 Fast-drying Epoxy Primer are listed below.Item No.is the most accurate form when ordering;Colour/colour codecorresponds to the actual colour (RAL, GSB are colour chart codes);Packaging SpecificationsFactory complete-set specification format. Colors not listed may be ordered against the colour card.
| Item No. | Colour / colour code | Packaging Specifications |
|---|---|---|
| EPA213 | Buff | 20 L |
This model has a total of1item numbers, all listed on this page; colours outside the table (including special colours and bulk packaging) can be confirmed by phone, delivery dates are advised according to the factory's current production schedule and stock. In the packaging specification, the "+" indicates the complete-set notation for two-component products (base + curing agent), subject to the factory specification; a "—" in the colour column denotes an auxiliary product, or that the item has no colour code in the factory system.